Experimental determination of interfacial energies for Ag2Al solid solution in the CuAl2-Ag2Al system
(IOP PUBLISHING LTD, 2009)
The equilibrated grain boundary groove shapes of solid solution Ag2Al in equilibrium with an Al-Cu-Ag liquid were observed from a quenched sample with a radial heat flow apparatus. The Gibbs-Thomson coefficient, solid-liquid ...
Variations of microhardness with the solidification processing parameters and thermo-electrical properties with the temperature in the Sn-Cu alloy
(REDAKCIA KOVOVE MATERIALY, 2009)
Sn-1.2wt.%Cu eutectic alloy was directionally solidified upward with different growth rates (2-78-136.36 mu m s(-1)) at a constant temperature gradient (2.69 K mm(-1)) and with different temperature gradients (2.69-8.88 K ...
The effect of composition on microhardness and determination of electrical and thermal properties in the Sn-Cu alloys
(SPRINGER, 2011)
Tin-copper of (99.99%) high purity alloys were directionally solidified upward with different compositions, C (o) , Sn-(1.2, 3, 6 and 15)wt% Cu under two different solidification conditions (temperature gradient (G) = 8 ...
Variation of microindentation hardness with solidification and microstructure parameters in the Al based alloys
(ELSEVIER SCIENCE BV, 2008)
The Al based alloys (Al-3 wt%Si, Al-3 wt%Cu and Al-1 wt%Ti) were prepared using metals of 99.99% high purity in the vacuum atmosphere. These alloys were directionally solidified upward with a constant growth rate (V = 0.008 ...
Investigation of directional solidified Al-Ti alloy
(ELSEVIER SCIENCE BV, 2009)
Al-1 wt% Ti alloy was directionally solidified upwards under argon atmosphere under the two conditions; with different temperature gradients (G = 2.20-5.82 K/mm) at a constant growth rate (V = 8.30 mu m/s) and with different ...
Dendritic growth of the binary succinonitrile-camphor system
(WORLD SCIENTIFIC PUBL CO PTE LTD, 2007)
Succinonitrile (SCN)-2wt% Camphor (CAMP) alloy was unidirectionally solidified with a constant temperature gradient (G=3.01 K/mm) at different growth rates (V=6.5- 113 mu m/s) and with a constant growth rate (V=6.5 mu m/s) ...
Investigation of the effect of solidification processing parameters on the rod spacings and variation of microhardness with the rod spacing in the Sn-Cu hypereutectic alloy
(SPRINGER, 2010)
Sn-3 wt% Cu hypereutectic alloy was prepared in a graphite crucible under the vacuum atmosphere. The samples were directionally solidified upwards under argon atmosphere with different temperature gradients (G = 4.24-8.09 ...
Experimental determination of solid-solid and solid-liquid interfacial energies of solid epsilon (CuZn5) in the Zn-Cu alloy
(ELSEVIER SCIENCE SA, 2009)
The equilibrated grain boundary groove shapes of solid epsilon; (CuZn5) in equilibrium with Zn-1.75 at.% Cu peritectic liquid and solid epsilon (CuZn5) in equilibrium with solid Zn solution (Zn-2.83 at.% Cu) were observed ...
Interfacial energy of solid In2Bi intermetallic phase in equilibrium with In-Bi eutectic liquid at 72 degrees C equilibrating temperature
(ELSEVIER SCIENCE INC, 2008)
A radial temperature gradient on the sample was established by heating from centre with a single heating wire and cooling the outside of sample at -10 degrees C with a heating/refrigerating circulating bath containing an ...
Characterization of a Directionally Solidified Sn-Pb-Sb Ternary Eutectic Alloy
(SPRINGER, 2015)
A Sn-40.5wt%Pb-2.6wt%Sb ternary eutectic alloy was prepared using a vacuum melting furnace and a casting furnace. The samples were directionally solidified at a constant growth rate (V = 16.5 mu m/s) under different ...