A Sn-40.5wt%Pb-2.6wt%Sb ternary eutectic alloy was prepared using a vacuum melting furnace and a casting furnace. The samples were directionally solidified at a constant growth rate (V = 16.5 mu m/s) under different ...

Al-5.7 wt% Ni eutectic alloy was directionally solidified upward with different temperature gradients (0.83-4.02 K/mm) at a constant growth rate (0.008 mm/s) and with different growth rates (0.008-0.483 mm/s) at a constant ...

Al-Cu-Ag eutectic alloy was directionally solidified upwards with different growth rates (1.83-498.25 mu m/s) at a constant temperature gradient (8.79 K/mm) and with different temperature gradients (3.99-8.79 K/mm) at a ...

This work presents the results of characterization of as solidified arc-melted Ni-Si and Co-Si alloys. The alloys of different compositions of the constitutions Ni, Co, and Si of purity of 99.99% were prepared by arc melting ...

Zinc-copper of (99.99%) high purity alloys were directionally solidified upward with different compositions, C-o, Zn-(0.7,1.5, 2.4 and 7.37) wt.% Cu under two different solidification conditions (G = 3.85 K/mm, V = 0.0083 ...

Zn-1.5wt.% Cu peritectic alloy was directionally solidified upward with different growth rates (8.41-661.11 mu m/s) at a constant temperature gradient (7.81 K/mm) and with different temperature gradients (1.99-7.81 K/mm) ...