Effect of solidification parameters on the microstructure of directionally solidified Sn-Bi-Zn lead-free solder
(KOREAN INST METALS MATERIALS, 2012)
Sn-Bi-Zn lead free solder alloy was directionally solidified upward at a constant temperature gradient (G=3.99 K/mm) with a wide range of growth rates (8.3-478.6 mu m/s) and at a constant growth rate (V=8.3 mu m/s) with a ...
Influence of temperature gradient and growth rate on the mechanical properties of directionally solidified Sn-3.5 wt% Ag eutectic solder
(SPRINGER, 2012)
The Sn-3.5 wt% Ag eutectic alloy was directionally solidified upward with a constant growth rate (V = 16.5 mu m/s) at different temperature gradients (G = 1.43-4.28 K/mm) and with a constant temperature gradient (G = 3.93 ...
Measurements of the microhardness, electrical and thermal properties of the Al-Ni eutectic alloy
(ELSEVIER SCI LTD, 2012)
Al-5.7 wt% Ni eutectic alloy was directionally solidified upward with different temperature gradients (0.83-4.02 K/mm) at a constant growth rate (0.008 mm/s) and with different growth rates (0.008-0.483 mm/s) at a constant ...
Variations of microhardness with solidification parameters and electrical resistivity with temperature for Al-Cu-Ag eutectic alloy
(ELSEVIER SCIENCE BV, 2012)
Al-Cu-Ag eutectic alloy was directionally solidified upwards with different growth rates (1.83-498.25 mu m/s) at a constant temperature gradient (8.79 K/mm) and with different temperature gradients (3.99-8.79 K/mm) at a ...