Experimental determination of interfacial energies for Ag2Al solid solution in the CuAl2-Ag2Al system
(IOP PUBLISHING LTD, 2009)
The equilibrated grain boundary groove shapes of solid solution Ag2Al in equilibrium with an Al-Cu-Ag liquid were observed from a quenched sample with a radial heat flow apparatus. The Gibbs-Thomson coefficient, solid-liquid ...
Experimental determination of solid-solid and solid-liquid interfacial energies of solid epsilon (CuZn5) in the Zn-Cu alloy
(ELSEVIER SCIENCE SA, 2009)
The equilibrated grain boundary groove shapes of solid epsilon; (CuZn5) in equilibrium with Zn-1.75 at.% Cu peritectic liquid and solid epsilon (CuZn5) in equilibrium with solid Zn solution (Zn-2.83 at.% Cu) were observed ...
Interfacial energy of solid In2Bi intermetallic phase in equilibrium with In-Bi eutectic liquid at 72 degrees C equilibrating temperature
(ELSEVIER SCIENCE INC, 2008)
A radial temperature gradient on the sample was established by heating from centre with a single heating wire and cooling the outside of sample at -10 degrees C with a heating/refrigerating circulating bath containing an ...
The effect of growth rate on microstructure and microindentation hardness in the In-Bi-Sn ternary alloy at low melting point
(ELSEVIER SCIENCE SA, 2009)
In-21.5 at.% Bi-17.8 at.% Sn ternary alloy which has 333 K melting point was directionally solidified upward with a constant temperature gradient (G = 0.91 K/mm) in a wide range of growth rates (3.2-157.1 mu m/s) with a ...
Determination of solid-liquid interfacial energies in the In-Bi-Sn ternary alloy
(IOP PUBLISHING LTD, 2008)
The equilibrated grain boundary groove shapes of solid In(2)Bi solution in equilibrium with the In-Bi-Sn eutectic liquid were observed from a quenched sample at 59 degrees C. The Gibbs-Thomson coefficient, solid-liquid ...
Measurement of solid-liquid interfacial energy in the In-Bi eutectic alloy at low melting temperature
(IOP PUBLISHING LTD, 2007)
The Gibbs-Thomson coefficient and solid-liquid interfacial energy of the solid In solution in equilibrium with In Bi eutectic liquid have been determined to be (1.46 +/- 0.07) x 10(-7) K m and (40.4 +/- 4.0) x 10(-3) J ...
Determination of interfacial energies of solid Sn solution in the In-Bi-Sn ternary alloy
(ELSEVIER SCIENCE INC, 2009)
The equilibrated grain boundary groove shapes of solid Sn solution (Sn-40.14 at.% In-16.11 at.% Bi) in equilibrium with the In-Bi-Sn liquid (In-21.23 at.% Bi-19.04 at.% Sn) were observed from the quenched sample at 59 ...
Dependency of Microstructural Parameters and Microindentation Hardness on the Temperature Gradient in the In-Bi-Sn Ternary Alloy with a Low Melting Point
(KOREAN INST METALS MATERIALS, 2008)
The ternary alloy In-21.5 at.% Bi-17.8 at.% Sn, which has a melting point of 60 degrees C, was directionally solidified upward with a constant growth rate (V = 3.2 mu m/s) and different temperature gradients (G = 0.91 K/mm ...