Experimental determination of interfacial energies for Ag2Al solid solution in the CuAl2-Ag2Al system
(IOP PUBLISHING LTD, 2009)
The equilibrated grain boundary groove shapes of solid solution Ag2Al in equilibrium with an Al-Cu-Ag liquid were observed from a quenched sample with a radial heat flow apparatus. The Gibbs-Thomson coefficient, solid-liquid ...
Investigation of the effect of solidification processing parameters on the rod spacings and variation of microhardness with the rod spacing in the Sn-Cu hypereutectic alloy
(SPRINGER, 2010)
Sn-3 wt% Cu hypereutectic alloy was prepared in a graphite crucible under the vacuum atmosphere. The samples were directionally solidified upwards under argon atmosphere with different temperature gradients (G = 4.24-8.09 ...
Experimental determination of solid-solid and solid-liquid interfacial energies of solid epsilon (CuZn5) in the Zn-Cu alloy
(ELSEVIER SCIENCE SA, 2009)
The equilibrated grain boundary groove shapes of solid epsilon; (CuZn5) in equilibrium with Zn-1.75 at.% Cu peritectic liquid and solid epsilon (CuZn5) in equilibrium with solid Zn solution (Zn-2.83 at.% Cu) were observed ...
Interfacial energy of solid In2Bi intermetallic phase in equilibrium with In-Bi eutectic liquid at 72 degrees C equilibrating temperature
(ELSEVIER SCIENCE INC, 2008)
A radial temperature gradient on the sample was established by heating from centre with a single heating wire and cooling the outside of sample at -10 degrees C with a heating/refrigerating circulating bath containing an ...
The effect of growth rate on microstructure and microindentation hardness in the In-Bi-Sn ternary alloy at low melting point
(ELSEVIER SCIENCE SA, 2009)
In-21.5 at.% Bi-17.8 at.% Sn ternary alloy which has 333 K melting point was directionally solidified upward with a constant temperature gradient (G = 0.91 K/mm) in a wide range of growth rates (3.2-157.1 mu m/s) with a ...
Effects of growth rate and temperature gradient on the microstructure parameters in the directionally solidified succinonitrile-7.5 wt.% carbon tetrabromide alloy
(ELSEVIER SCIENCE SA, 2008)
Succinonitrile (SCN)-7.5 wt.% carbon tetrabromide (CTB) alloy was unidirectionally solidified with a constant growth rate (V = 33 mu m/s) at five different temperature gradients (G = 4.1-7.6 K/mm) and with a constant ...
Determination of solid-liquid interfacial energies in the In-Bi-Sn ternary alloy
(IOP PUBLISHING LTD, 2008)
The equilibrated grain boundary groove shapes of solid In(2)Bi solution in equilibrium with the In-Bi-Sn eutectic liquid were observed from a quenched sample at 59 degrees C. The Gibbs-Thomson coefficient, solid-liquid ...
Variations of microhardness with solidification parameters and electrical resistivity with temperature for Al-Cu-Ag eutectic alloy
(ELSEVIER SCIENCE BV, 2012)
Al-Cu-Ag eutectic alloy was directionally solidified upwards with different growth rates (1.83-498.25 mu m/s) at a constant temperature gradient (8.79 K/mm) and with different temperature gradients (3.99-8.79 K/mm) at a ...
Thermal conductivity and interfacial energies of solid Sn in the Sn-Cu alloy
(ELSEVIER SCIENCE BV, 2010)
The equilibrated grain boundary groove shapes of solid Sn in equilibrium with the Sn-Cu eutectic liquid were observed from a quenched sample. The Gibbs-Thomson coefficient, solid-liquid interfacial energy and grain boundary ...
A study of microstructure and solidification behaviour of Zn-Cu alloy
(REDAKCIA KOVOVE MATERIALY, 2010)
Zn-1.5wt.%Cu peritectic alloy was prepared in a graphite crucible under a vacuum atmosphere. Unidirectional solidification of Zn-1.5wt.%Cu peritectic alloy was carried out with the Bridgman method by using metals of 99.99 ...