Investigation of the effect of solidification processing parameters on the rod spacings and variation of microhardness with the rod spacing in the Sn-Cu hypereutectic alloy

Cadirli, E.; Boyuk, U.; Engin, S.; Kaya, H.; Marasli, N.; Keslioglu, K.; Ulgen, A. (SPRINGER, 2010)

Sn-3 wt% Cu hypereutectic alloy was prepared in a graphite crucible under the vacuum atmosphere. The samples were directionally solidified upwards under argon atmosphere with different temperature gradients (G = 4.24-8.09 ...

Investigation of the effect of solidification processing parameters on microhardness and determination of thermo-physical properties in the Zn-Cu peritectic alloy

Boyuk, U.; Kaya, H.; Cadirli, E.; Marasli, N.; Ulgen, A. (ELSEVIER SCIENCE SA, 2010)

Zn-1.5wt.% Cu peritectic alloy was directionally solidified upward with different growth rates (8.41-661.11 mu m/s) at a constant temperature gradient (7.81 K/mm) and with different temperature gradients (1.99-7.81 K/mm) ...