Investigation of the effect of solidification processing parameters on the rod spacings and variation of microhardness with the rod spacing in the Sn-Cu hypereutectic alloy
(SPRINGER, 2010)
Sn-3 wt% Cu hypereutectic alloy was prepared in a graphite crucible under the vacuum atmosphere. The samples were directionally solidified upwards under argon atmosphere with different temperature gradients (G = 4.24-8.09 ...
Investigation of the effect of solidification processing parameters on microhardness and determination of thermo-physical properties in the Zn-Cu peritectic alloy
(ELSEVIER SCIENCE SA, 2010)
Zn-1.5wt.% Cu peritectic alloy was directionally solidified upward with different growth rates (8.41-661.11 mu m/s) at a constant temperature gradient (7.81 K/mm) and with different temperature gradients (1.99-7.81 K/mm) ...
Experimental investigation of the effect of solidification processing parameters on the rod spacings in the Sn-1.2 wt.% Cu alloy
(ELSEVIER SCIENCE SA, 2009)
Sn-1.2 wt.% Cu alloy was prepared in a graphite crucible under the vacuum atmosphere. The samples were directionally solidified upwards under argon atmosphere with different temperature gradients (G = 2.69-8.88 K/mm) at a ...