The Dependence of Lamellar Spacings and Microhardness on the Growth Rate in the Directionally Solidified Bi-43 wt.% Sn Alloy at a Constant Temperature Gradient
(KOREAN INST METALS MATERIALS, 2009)
Bi-43 wt.% Sn eutectic samples were directionally solidified upward with five different growth rates (V = 8.3-164.8 mu m/s) at a constant temperature gradient (G = 3.55 K/mm) in a Bridgman type directional solidification ...
Dependency of Microstructural Parameters and Microindentation Hardness on the Temperature Gradient in the In-Bi-Sn Ternary Alloy with a Low Melting Point
(KOREAN INST METALS MATERIALS, 2008)
The ternary alloy In-21.5 at.% Bi-17.8 at.% Sn, which has a melting point of 60 degrees C, was directionally solidified upward with a constant growth rate (V = 3.2 mu m/s) and different temperature gradients (G = 0.91 K/mm ...